O le a le mea fa'asalalau e mafai ona tatalia e le pamu fa'amaneta fa'amaneta fa'amaneta?

O pamu maneta uamea uamea e iai le faatinoga o le anti-corrosion. u'amea u'amea u'amea e aofia ai 304, 316L, ma isi mea e lua e masani ona fa'aaogaina i pamu maneta uamea. Mo le tuʻuina atu o vai faʻafefete malosi, o fea le faʻatapulaʻaina o le faʻaogaina o le faʻaogaina o le uʻamea uʻamea? Le auala e feaveaia E valu ituaiga autu o le pala i u'amea maneta pamu mea: electrochemical corrosion, corrosion toniga, intergranular corrosion, pitting corrosion, crevice corrosion, stress corrosion, ofu pala, ma cavitation corrosion.

1. A'a ole lua
Pitting corrosion o se ituaiga o pala i totonu. Ona o le faʻaleagaina faʻapitonuʻu o le uʻamea passivation ata, ua vave ona fausia lua hemispherical i se vaega faʻapitonuʻu o le uamea, lea e taʻua o pitting corrosion. Ole pala ole lua e mafua ile CL￣. Ina ia puipuia le pala, e mafai ona faʻaogaina le sila (e masani lava 2.5% Mo), ma faʻatasi ai ma le faʻateleina o le CL￣ anotusi ma le vevela, e tatau foi ona faʻatuputeleina le mea o loʻo iai Mo.

2. A'a gaogao
Crevice corrosion o se ituaiga o corrosion i le lotoifale, lea e faasino i le corrosion e mafua mai i le faaleagaina i le lotoifale o le uʻamea passivation ata ona o le faaitiitia o le okesene i totonu ma (po o) pH faaitiitia i le gaʻo pe a uma ona tumu le ga i vai corrosive. E masani ona tupu le pala u'amea u'amea i le vaifofo CL￣. O le a'a o le ga'o ma le pala e lua e tutusa lelei lava i le faiga o le faiga. E mafua uma i le matafaioi a le CL￣ ma le faʻaleagaina i le lotoifale o le ata pasi. Faatasi ai ma le faateleina o le CL￣ mea e aofia ai ma le si'itia o le vevela, e fa'atupula'ia ai le fa'aleagaina o le va. O le fa'aogaina o u'amea e maualuga le Cr ma le Mo e mafai ona taofia pe fa'aitiitia ai le pala.

3. A'a tutusa
O le pala tutusa e faasino i le pala o kemikolo tutusa o le u'amea atoa pe a fa'afeso'ota'i le vai u'amea. O le ituaiga e sili ona taatele ma sili ona leaga o le pala.
O faiga e puipuia ai le a'a tutusa o le: fa'aaoga mea talafeagai (e aofia ai le u'amea), ma mafaufau ia lava alauni a'a ile mamanu o pamu.

4. Cavitation corrosion
O le pala e mafua mai le cavitation i totonu o le pamu mageta e ta'ua o le cavitation corrosion. O le auala sili ona aoga ma faigofie e puipuia ai le pala o le cavitation o le puipuia lea o le cavitation mai le tupu. Mo pamu e masani ona mafatia i le cavitation i le taimi o le taotoga, ina ia aloese mai le faaleagaina o le cavitation, e mafai ona faʻaaogaina mea e faʻafefete ai le cavitation, e pei o le uʻamea malo, phosphor bronze, austenitic stainless steel, 12% chromium steel, ma isi.

5. Fa'amamafa le pala
Stress corrosion e faasino i se ituaiga o eleelea e mafua mai i le gaioiga soofaatasi o le atuatuvale ma le siosiomaga corrosive.
Austenitic Cr-Ni u'amea e sili atu ona fa'amamafa i le pala ile CL~ medium. Faatasi ai ma le faateleina o le CL￣ mea e aofia ai, vevela ma le atuatuvale, e sili atu ona tupu le pala. E masani lava, e le tupu le pala o le mamafa i lalo ole 70 ~ 80 ° C. O le fuataga e puipuia ai le faʻalavelave faʻalavelave o le faʻaaogaina lea o austenitic Cr-Ni uamea ma maualuga Ni mea (Ni o 25% ~ 30%).

6. Eleele palapala eletise
Electrochemical corrosion o loʻo faʻatatau i le faʻagasologa eletise lea e faʻapipiʻi ai le faʻafesoʻotaʻi o uʻamea eseese e fausia ai se maa ona o le eseesega i le eletise eletise i le va o uʻamea, ma mafua ai le pala o le uamea anode.
Faiga e puipuia ai le pala eletise: Muamua, e sili ona lelei le faʻaaogaina o le mea uʻamea tutusa mo le tafe o le pamu; lona lua, faʻaaoga anodes taulaga e puipuia ai le uʻamea cathode.

7. A'a a'ia'i
Intergranular corrosion o se ituaiga o corrosion i le lotoifale, lea e masani ona faasino i le precipitation o chromium carbide i le va o fatu uamea stainless. O le pala ole intergranular e matua'i pala i mea uamea. O mea fa'atasi ma intergranular corrosion e leiloa lona malosi ma palasitika toetoe lava atoa.
O faiga e puipuia ai le pala i totonu o le vaeluagalemu o le: fa'amama u'amea u'amea, po'o le fa'aogaina o le u'amea u'amea ultra-maualalo (C<0.03%).

8. La'ei ma pala
Abrasion corrosion e faasino i se ituaiga o eleelea o le suavai maualuga-saosaoa i luga o le uamea. Ole tafia ole suavai e ese mai ile tafia ole eleele e mafua mai i ni mea malō ile ala.
'ese'ese meafaitino e 'ese'ese mea fa'a'au'au ma fa'ama'i. O le fa'asologa o le ofuina ma le pala mai le leaga i le lelei o le: ferritic Cr sila